ASTM A213 Alloy Steel Tube
| Model No. : | BT09 |
|---|---|
| status : | New |
Produktbeskrivning
ASTM A213 Specificerad för sömlösa ferritiska och Austenitiska legeringsstålpannor, överhettare och värmeväxlarrör.
Legeringsklass: T2, T5, T9, T11, T12, T91, T92
Ytterdiameter: 28mm-168mm
Väggtjocklek: 2mm-30mm
ASTM A213 kemisk sammansättning av legerat stålrör:
|
Grade |
C |
Mn |
P |
S |
Si |
Cr |
Mo |
V |
N |
Ni |
Al |
Nb |
W |
|
T2 |
0.10-0.20 |
0.30-0.61 |
0.025 max |
0.025 max |
0.10-0.30 |
0.50-0.81 |
0.44-0.65 |
|
|
|
|
|
|
|
T5 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.50 max |
4.00-6.00 |
0.45-0.65 |
|
|
|
|
|
|
|
T9 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.25-1.00 |
8.0-10.0 |
0.90-1.10 |
|
|
|
|
|
|
|
T11 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
|
|
|
|
|
|
T12 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
|
|
|
|
|
|
T22 |
0.05-0.15 |
0.30-0.60 |
0.025 max |
0.025 max |
0.50 max |
1.90-2.60 |
0.87-1.13 |
|
|
|
|
|
|
|
T91 |
0.08-0.12 |
0.30-0.60 |
0.020 max |
0.010 max |
0.20-0.50 |
8.00-9.50 |
0.85-1.05 |
0.18-0.25 |
0.03-0.07 |
0.40 max |
0.04 max |
0.06-0.10 |
|
|
T92 |
0.07-0.13 |
0.30-0.60 |
0.020 max |
0.010 max |
0.50 max |
8.50-9.50 |
0.30-0.60 |
.015-0.25 |
0.03-0.07 |
0.40 max |
0.04 max |
0.04-0.09 |
1.50-2.00 |
ASTM A213 legerat stålrör mekanisk egenskapstabell:
|
Grade |
Tensile Strength, Mpa |
Yield Strength, Mpa |
Elongation, % |
Hardness, HB |
|
T2 |
415 min |
205 min |
30 min |
163 max |
|
T5 |
415 min |
205 min |
30 min |
163 max |
|
T9 |
415 min |
205 min |
30 min |
179 max |
|
T11 |
415 min |
205 min |
30 min |
179 max |
|
T12 |
415 min |
205 min |
30 min |
179 max |
|
T22 |
415 min |
205 min |
30 min |
163 max |
|
T91 |
585 min |
415 min |
20 min |
250 max |
|
T92 |
585 min |
415 min |
20 min |
250 max |
ASTM A213 legerat stålrör yttre diameter tolerans:
|
Method |
Outside Diameter,mm |
Tolerance, mm |
|
Hot Rolled |
OD=101.6 |
+0.4 / -0.8 |
|
101.6<OD=190.5 |
+0.4 / -1.2 |
|
|
190.5<OD=228.6 |
+0.4 / -1.6 |
|
|
Cold Drawn |
OD<25.4 |
±0.10 |
|
25.4=OD=38.1 |
±0.15 |
|
|
38.1<OD<50.8 |
±0.20 |
|
|
50.8=OD<63.5 |
±0.25 |
|
|
63.5=OD<76.2 |
±0.30 |
|
|
76.2=OD=101.6 |
±0.38 |
|
|
101.6<OD=190.5 |
?0.38 / -0.64 |
|
|
190.5<OD=228.6 |
?0.38 / -1.14 |
|
ASTM A213 väggtjocklek av legerat stålrör:
|
Method |
Outside Diameter, mm |
Tolerance, % |
|
Hot Rolled |
OD=101.6,WT=2.4 |
+40 / -0 |
|
OD=101.6,2.4<WT=3.8 |
+35 / -0 |
|
|
OD=101.6,3.8<WT=4.6 |
+33 / -0 |
|
|
OD=101.6,WT>4.6 |
+28 / -0 |
|
|
OD>101.6,2.4<WT=3.8 |
+35 / -0 |
|
|
OD>101.6,3.8<WT=4.6 |
+33 / -0 |
|
|
OD>101.6,WT>4.6 |
+28 / -0 |
|
|
Cold Drawn |
OD=38.1 |
+20 / -0 |
|
OD>38.1 |
+22 / -0 |
|
UNIDUS är en av de ledande tillverkarna och leverantörerna av ASTM A213 legerat stålrör, om du vill köpa eller importera A213 T2, A213 T5, A213 T9, A213 T11, A213 T12, A213 T22, A213 T91, A213 T92 legerat stålrör, tack kontakta oss gärna.