YR802 Chlorination of rutile titanium dioxide, is the
base material for oxidative chlorination output by silicon,
the aluminum coated, and then formed by the organic
surface treatment of titanium dioxide pigment, Has good
color and blue phase,good weather resistance, hiding
power, stability.
Using: paints, rubber, plastics, inks and paper industries.
Standard: GB/T1706-2006 GB/T 1250
Introduction:
Package: 25kg/Paper-plastic bag or 1000kgs/bag


Item                                                                          Data
Surface treatment                                            Al. Si compounds
TiO2 content ≥                                                           90.5%
Rutile content≥                                                           99%
Oil Absorption g/100g≤                                                 18
brightness( L*) ≥                                                            97
Tone, white( b*) ≤                                                         1.6
Oil Dispersion( Haegeman value) ≥                              6.75
Relative Scattering power ≥                                           98
SCX(gray paint tone) ≥                                                   5.5
Tinctorial Strength TCS( Reynolds )≥                            2050
Water Suspension PH value                                            6-8
Residue on Sieve( 45μm sieve) ≤                                  0.05%
105ºC Volatile Matter ≤                                                   0.50%
Water Suspension Resistivity Ω·m                                  120
D50( μm)                                                                           0.34